It is an epoxy resin-based, two-component, surface-tolerant, high build, self-priming mastic coating containing zinc phosphate, cured with a modified polyamine hardener. It can be applied in high film thicknesses, adheres very well to the applied surface and gives a flexible film.
It can be applied to all metal surfaces. It has been developed as a protective coating for new steel surfaces and solid and old painted surfaces. It can also be applied to damp surfaces. It is used as a high build surface tolerance single coat coating of protective paint systems where UV resistance is not important. It is used as a primer/undercoat where UV resistance is important. It is used as a single layer coating on structural steels, bridges, underwater and above water parts of metal surfaces, underwater surfaces of ships, chemical industry facilities.
| Density (20°C , gr/cm³ ) | : | 1,30 - 1,50 (depending on color) |
| Drying Time (20°C) | : | |
| Powder drying : 6-7 hours | ||
| Full drying : 7 days | ||
| Solid Matter | : | 80,0 - 84,0 (depends on color) |
| Thinner | : | Epoxy Thinner (971-0711) |
| Thinning Rate | : | % 10-15 |
| Gloss | : | Semi Matte |
| Hardener | : | Epoxy Hardener (849-0085) |
| Mixing Ratio ( By Weight ) | : | 7/1 |
| Pot Life (20° C) | : | 2 hours |
| Paintable Area | : | When applied with a dry film thickness of 100 µ, an area between 1 kg and 6 m² can be covered. (Excluding losses) |
It is applied as a spray (air-airless spray). All surfaces to be painted must be clean and dry. After 13-14 hours, the top coat of paint can be applied by patting and sanding. Recommended application thickness: 100 µ kfk (dry film thickness)